Material de resina de poliuretano para sandálias de linhas de fundição
obtenha o ultimo preçoTipo de pagamento: | L/C,T/T |
Incoterm: | FOB,CIF |
Quantidade de pedido mínimo: | 1000 Kilogram |
transporte: | Ocean,Land |
porta: | Shanghai |
Tipo de pagamento: | L/C,T/T |
Incoterm: | FOB,CIF |
Quantidade de pedido mínimo: | 1000 Kilogram |
transporte: | Ocean,Land |
porta: | Shanghai |
Modelo: A-9088W,B-6088
marca: Xuchuan Chemical
Lugar De Origem: China
Tipos De: Resina Sintética e Plásticos
Name Of Product: A-9088W/B-6088
Keywords: pu molding,polyurethane resin for casting,material straps for sandals
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line
Appearance: liquid
Application: shoe sole
DESCRIÇÃO DO PRODUTO
Matérias -primas de poliuretano
Application | shoe sole |
Keywords | pu molding,polyurethane resin for casting,material straps for sandals |
A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) | 100/100~102 |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 30~40 |
Free Rise Foam Density(g/cm3) | 0.21~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | Demold Time(min) |
Molded Density (g/cm3) | 0.35~0.60 |
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line |
|||||||
Application: Outsole, slippers, wedge shoes |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-9080W |
Cream,White,liquid |
1000~1300 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-6088 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Materials preheat |
|||||||
A-9080W: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-6088: preheated at 50~60℃ for 6~8 hours. |
|||||||
Typical processing parameters & Reaction parameter. |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/100~102 |
6~8 |
30~40 |
0.21~0.26 |
45~55 |
5~7 |
The adding content of C-2 should be 210g±10g/18kg. |
|||||||
The adding content of water should be 0~80g/18kg according to the reality. |
|||||||
The adding content of hardener should be 0~1200g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Williams abrasion |
/ |
Physical properties |
0.35~0.60 |
60~88 |
4~7 |
200~300 |
11~20 |
130~200 |
/ |
Demold time may be prolonged with the increase of sole thickness. |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Isocianato de poliol para a sola média
Xuchuan Chemical estabelecido em 2007, o capital registrado da empresa é de RMB 500 milhões. Os principais produtos são todos os intervalos de poliolol, resina de poliuretano para sapatos, resinas de poliuretano à base de água e sem solventes para couro artificial, adesivos de ligação de poliuretano e adesivos de fusão a quente de poliuretano.
Agora, o Xuchuan tem 4 bases de produção modernas, a capacidade de produção atingiu 630.000 toneladas por ano, produtos exportados para 32 países e regiões do mundo.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.